Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 18
Page 386
... zirconium in 90 % nitric acid at room temperatures . It has been shown that careful control of texture , surface condition ( scratching , cleaning and oxide coating ) and / or applied stress can effectively lead to the prevention of SCC ...
... zirconium in 90 % nitric acid at room temperatures . It has been shown that careful control of texture , surface condition ( scratching , cleaning and oxide coating ) and / or applied stress can effectively lead to the prevention of SCC ...
Page 395
... zirconium in HNO3 moves toward the noble direction . However , as shown in Fig . 1 , the open circuit potentials of zirconium electrode in HF - containing 90 % HNO3 ... Zirconium in 90 % Nitric Acid when 80g 395 T.L. You Corrosion Reviews.
... zirconium in HNO3 moves toward the noble direction . However , as shown in Fig . 1 , the open circuit potentials of zirconium electrode in HF - containing 90 % HNO3 ... Zirconium in 90 % Nitric Acid when 80g 395 T.L. You Corrosion Reviews.
Page 396
Susceptibility of Zirconium in 90 % Nitric Acid when 80g of zirconium sponge ( an excessive amount ) was added to 500cc of this solution . The beneficial effect of HF on SCC of zirconium in 90 % HNO3 is shown in Table 6. Table 6 shows ...
Susceptibility of Zirconium in 90 % Nitric Acid when 80g of zirconium sponge ( an excessive amount ) was added to 500cc of this solution . The beneficial effect of HF on SCC of zirconium in 90 % HNO3 is shown in Table 6. Table 6 shows ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90