Page 386
... zirconium in 90 % HNO3 . Heat treating at 760 ° C , 880 ° C , or 1000 ° C does not seem to improve the SCC resistance However , if the potential of zirconium is maintained at 500mV or lower , or 200 ppm of HF is added , zirconium's SCC ...
... zirconium in 90 % HNO3 . Heat treating at 760 ° C , 880 ° C , or 1000 ° C does not seem to improve the SCC resistance However , if the potential of zirconium is maintained at 500mV or lower , or 200 ppm of HF is added , zirconium's SCC ...
Page 395
... zirconium electrode in HF - containing 90 % HNO3 solutions move toward the active direction . The addition of 800 ppm zirconium sponge alone does not reverse the trend of the open circuit potential of zirconium in 90 % HNO3 as shown in ...
... zirconium electrode in HF - containing 90 % HNO3 solutions move toward the active direction . The addition of 800 ppm zirconium sponge alone does not reverse the trend of the open circuit potential of zirconium in 90 % HNO3 as shown in ...
Page 396
Susceptibility of Zirconium in 90 % Nitric Acid when 80g of zirconium sponge ( an excessive amount ) was added to 500cc of this solution . The beneficial effect of HF on SCC of zirconium in 90 % HNO3 is shown in Table 6. Table 6 shows ...
Susceptibility of Zirconium in 90 % Nitric Acid when 80g of zirconium sponge ( an excessive amount ) was added to 500cc of this solution . The beneficial effect of HF on SCC of zirconium in 90 % HNO3 is shown in Table 6. Table 6 shows ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90