Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 40
Page 388
... weld metals is very difficult to control . Moreover , weld metals of zirconium are more susceptible to SCC in concentrated HNO3 than wrought products / 4 , 9 / . Therefore , for HNO3 service , an additional protective measure will still ...
... weld metals is very difficult to control . Moreover , weld metals of zirconium are more susceptible to SCC in concentrated HNO3 than wrought products / 4 , 9 / . Therefore , for HNO3 service , an additional protective measure will still ...
Page 389
... Weld 310 100 133 ; 278 279 90 ( 616 ) ; ( 616 ) < 479 ; < 479 ( 479 ) ; ( 479 ) 207 66.6 ( 616 ) ; ( 616 ) ( 1 ) Number in parenthesis is the time tested for specimens that did not fail . transverse weld ( not a circumference weld ) . Weld ...
... Weld 310 100 133 ; 278 279 90 ( 616 ) ; ( 616 ) < 479 ; < 479 ( 479 ) ; ( 479 ) 207 66.6 ( 616 ) ; ( 616 ) ( 1 ) Number in parenthesis is the time tested for specimens that did not fail . transverse weld ( not a circumference weld ) . Weld ...
Page 68
... welds required for the bolts , weld defects may Occur . 4.2 Construction New Construction . For new construction , solid alloy plate , clad plate , or an attached liner can be used . Retrofit Construction . For retrofit or repair ...
... welds required for the bolts , weld defects may Occur . 4.2 Construction New Construction . For new construction , solid alloy plate , clad plate , or an attached liner can be used . Retrofit Construction . For retrofit or repair ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90