... toxicant . In service , the toxicant leaching takes place by a complex mechanism which involves permeation of sea water through the film , dissolution of the toxicant , the outward diffusion of the dissolved substance and the final ...
... toxicant . In service , the toxicant leaching takes place by a complex mechanism which involves permeation of sea water through the film , dissolution of the toxicant , the outward diffusion of the dissolved substance and the final ...
Page 98
... toxicant and on its leaching rate from the film when the paint film is in contact with sea water . This value is defined as the quantity of toxicant released from a considered area in a determined period of time and expressed as μg.cm2 ...
... toxicant and on its leaching rate from the film when the paint film is in contact with sea water . This value is defined as the quantity of toxicant released from a considered area in a determined period of time and expressed as μg.cm2 ...
Page 99
... Toxicant dissolution starts on the film surface , forming the mentioned toxic layer at the coat / sea water interface . In the soluble matrix paints , binder solubilization favours the obtention of an adequate toxicant leaching rate ...
... Toxicant dissolution starts on the film surface , forming the mentioned toxic layer at the coat / sea water interface . In the soluble matrix paints , binder solubilization favours the obtention of an adequate toxicant leaching rate ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90