Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 93
Page 402
Behavior of Sintered Stainless Steel ABSTRACT The influence of Cu , Ni and Pd on the corrosion behaviour of hot pressed sintered stainless steel of type 316 in H2SO4 solution was investigated . It was found that Cu addition improve the ...
Behavior of Sintered Stainless Steel ABSTRACT The influence of Cu , Ni and Pd on the corrosion behaviour of hot pressed sintered stainless steel of type 316 in H2SO4 solution was investigated . It was found that Cu addition improve the ...
Page 403
... stainless steel as compared to wrought stainless steel is mainly caused by the inter- connected open pores . Due to electrolyte stagnation in the intercon- nected open pores , hydrogen concentration cells were evolved between the ...
... stainless steel as compared to wrought stainless steel is mainly caused by the inter- connected open pores . Due to electrolyte stagnation in the intercon- nected open pores , hydrogen concentration cells were evolved between the ...
Page 410
... stainless steel . The potentiodynamic behaviour of hot pressed and sintered stainless steel demonstrates high passivation current density and practically passivation processes do not occur . High efficiency of passivation is observed ...
... stainless steel . The potentiodynamic behaviour of hot pressed and sintered stainless steel demonstrates high passivation current density and practically passivation processes do not occur . High efficiency of passivation is observed ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90