Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 13
Page 170
... soil resistivity with soil bar and bridge in bottom of hole . If soil resistivity is 10K OHM - CM or less , install a zinc anode . Otherwide install galvomag . 3. Connect anodes to structure with a temporary clamp . 4. Bridge clamp ...
... soil resistivity with soil bar and bridge in bottom of hole . If soil resistivity is 10K OHM - CM or less , install a zinc anode . Otherwide install galvomag . 3. Connect anodes to structure with a temporary clamp . 4. Bridge clamp ...
Page 170
... soil resistivity with soil bar and bridge in bottom of hole . If soil resistivity is 10K OHM - CM or less , install a zinc anode . Otherwide install galvomag . 3. Connect anodes to structure with a temporary clamp . 4. Bridge clamp ...
... soil resistivity with soil bar and bridge in bottom of hole . If soil resistivity is 10K OHM - CM or less , install a zinc anode . Otherwide install galvomag . 3. Connect anodes to structure with a temporary clamp . 4. Bridge clamp ...
Page 188
... soil resistivity . Even though the soils involved were of low aggressivity , steel grids suffered relatively high corrosion rates , specially when in contact with bentonite backfill , where values of up to 37 mdd were observed . Their ...
... soil resistivity . Even though the soils involved were of low aggressivity , steel grids suffered relatively high corrosion rates , specially when in contact with bentonite backfill , where values of up to 37 mdd were observed . Their ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90