Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 69
Page 405
The open - circuit potential of samples sintered for 2h and exposed to IN H2SO4 solution at room temperature is presented in Fig . 1. The potential of the samples containing Cu at various concentrations reaches a value of about + 200mV ...
The open - circuit potential of samples sintered for 2h and exposed to IN H2SO4 solution at room temperature is presented in Fig . 1. The potential of the samples containing Cu at various concentrations reaches a value of about + 200mV ...
Page 406
... samples after exposure to INH2SO4 solution for 150h . After the exposure to the corrosive environment , the polarization behaviour of samples containing various concentrations of Cu becomes similar . XPS measurements show that surface ...
... samples after exposure to INH2SO4 solution for 150h . After the exposure to the corrosive environment , the polarization behaviour of samples containing various concentrations of Cu becomes similar . XPS measurements show that surface ...
Page 410
... samples containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples ...
... samples containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90