Page 92
... rosin or gum rosin , Table II ) Table 2 : General characteristics of WW rosin Density at 20 ° C , g.ml1 . .1.08 Melting point , ° C .. Saponification value . 130 175 Iodine value .. Acid value 115 152 Ester number 23 Volatile materials ...
... rosin or gum rosin , Table II ) Table 2 : General characteristics of WW rosin Density at 20 ° C , g.ml1 . .1.08 Melting point , ° C .. Saponification value . 130 175 Iodine value .. Acid value 115 152 Ester number 23 Volatile materials ...
Page 123
and Beatriz del Amo The different vehicles had the following values : Rosin / phenolic varnish ratio , by weight Acid value 2/1 3/1 4/1 5/1 mg KOH.g " 106.8 120.1 128.1 133.4 These results are consistent with the WW rosin content in ...
and Beatriz del Amo The different vehicles had the following values : Rosin / phenolic varnish ratio , by weight Acid value 2/1 3/1 4/1 5/1 mg KOH.g " 106.8 120.1 128.1 133.4 These results are consistent with the WW rosin content in ...
Page 147
... rosin ( gum rosin ) 10.7 9.5 12.2 10.8 Grade 10 chlorinated rubber - 6.1 7.2 Grade 20 chlorinated rubber 5.3 9.5 - - 42 % chlorinated paraffin 2.3 4.1 2.6 3.1 Castor oil 1.2 1.2 1.0 1.1 Additives * 0.9 0.9 1.8 2.0 Solvents and thinners ...
... rosin ( gum rosin ) 10.7 9.5 12.2 10.8 Grade 10 chlorinated rubber - 6.1 7.2 Grade 20 chlorinated rubber 5.3 9.5 - - 42 % chlorinated paraffin 2.3 4.1 2.6 3.1 Castor oil 1.2 1.2 1.0 1.1 Additives * 0.9 0.9 1.8 2.0 Solvents and thinners ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90