Page 82
and Decorative Purposes TABLE 6 : Properties of obtained decorative coatings Wear Electrolyte Resistance Porosity ( no . of rev . ) ( di / dV A / V ) Hardness Corrosion ( Hv ) Resistance Microanalys . Acidic I 2.54 x 10 270 320 -3 ( 8 x ...
and Decorative Purposes TABLE 6 : Properties of obtained decorative coatings Wear Electrolyte Resistance Porosity ( no . of rev . ) ( di / dV A / V ) Hardness Corrosion ( Hv ) Resistance Microanalys . Acidic I 2.54 x 10 270 320 -3 ( 8 x ...
Page 327
Either rapid recovery of passivity in the reducing solution or a nonrequirement of passivity for its resistance ( Bierman and ... any modified alloy must be hard , chemically resistant , and still remain in the “ family " framework .
Either rapid recovery of passivity in the reducing solution or a nonrequirement of passivity for its resistance ( Bierman and ... any modified alloy must be hard , chemically resistant , and still remain in the “ family " framework .
Page 403
It was concluded that the low corrosion resistance of hot pressed stainless steel as compared to wrought stainless steel is mainly caused by the interconnected open pores . Due to electrolyte stagnation in the intercon . nected open ...
It was concluded that the low corrosion resistance of hot pressed stainless steel as compared to wrought stainless steel is mainly caused by the interconnected open pores . Due to electrolyte stagnation in the intercon . nected open ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy aluminum analysis anodic application base changes chemical cleaning coatings combination compared composition concentration conclusion considered containing copper corrosion Corrosion Control curve density deposits described determine direct effect electrochemical electron Engineering environment equipment evaluation example experimental expert system factor field Figure function given higher important increase industry inhibitor ions Israel knowledge layer less limited materials measurements mechanical metal method observed obtained operation organic oxide paint passivation performance plant plating polarization possible potential practical present problems properties protection Radioactive Tracer reduce reference reported resistance REVIEWS rules runs rust samples selection shown shows solution specific specimen stainless steel standard structure surface Table technique Technology temperature tube values welding