Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 85
Page 281
... potential . The first operation consists in reading the open circuit potential EM . This is done through " READE " command which employs an integration time of 80 ms . Once the value of Eм has been read , the electrochemical system is ...
... potential . The first operation consists in reading the open circuit potential EM . This is done through " READE " command which employs an integration time of 80 ms . Once the value of Eм has been read , the electrochemical system is ...
Page 394
... potentials below 700 mV , Of course , potential is not the only factor dictating SCC susceptibility . However , when the potential was controlled at 500 mVSCE , SCC of zirconium including weld metal was effectively avoided . Also , both ...
... potentials below 700 mV , Of course , potential is not the only factor dictating SCC susceptibility . However , when the potential was controlled at 500 mVSCE , SCC of zirconium including weld metal was effectively avoided . Also , both ...
Page 405
... potentials lower than -250mV ( SCE ) . The steady open - circuit potential of the samples containing Cu [ -200mV ( SCE ) ] is similar to that of wrought plate stainless steel of type AISI 316 / 2 / . The weight loss of the samples ...
... potentials lower than -250mV ( SCE ) . The steady open - circuit potential of the samples containing Cu [ -200mV ( SCE ) ] is similar to that of wrought plate stainless steel of type AISI 316 / 2 / . The weight loss of the samples ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90