Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 39
Page 210
... pitting , thinning and stress corrosion cracking ( SCC ) . The bottom scale in the figure shows how the pH range is subdivided into ranges of certainty with respect to a particular conclusion based on environmental factors ...
... pitting , thinning and stress corrosion cracking ( SCC ) . The bottom scale in the figure shows how the pH range is subdivided into ranges of certainty with respect to a particular conclusion based on environmental factors ...
Page 333
... Pitting and crevice corrosion No pitting was observed on CED - H3PO4 systems . Pitting was found on a rather comparable alloy CD - 4 . Corrosion was observed under the packing of a valve cast from CED . This may be crevice corrosion ...
... Pitting and crevice corrosion No pitting was observed on CED - H3PO4 systems . Pitting was found on a rather comparable alloy CD - 4 . Corrosion was observed under the packing of a valve cast from CED . This may be crevice corrosion ...
Page 295
... pitting tendency of the materials was conducted by running the static anodic curves as previously explained . The results for Cu - Ni 70/30 appear in Fig . 6. The pitting potential is found at 100 mV -100 -200 ER Aged Aged . S ...
... pitting tendency of the materials was conducted by running the static anodic curves as previously explained . The results for Cu - Ni 70/30 appear in Fig . 6. The pitting potential is found at 100 mV -100 -200 ER Aged Aged . S ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90