Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 66
Page 120
... oxide , was 99.84 per cent . During storage and previous to paint preparation , the composition of cuprous oxide had changed with an increase of the amount of Cu ° and Cu ( II ) . Within 10 days the metallic copper reached a ...
... oxide , was 99.84 per cent . During storage and previous to paint preparation , the composition of cuprous oxide had changed with an increase of the amount of Cu ° and Cu ( II ) . Within 10 days the metallic copper reached a ...
Page 126
... oxidation of cuprous oxide . As was observed during extender dispersion , increased cuprous oxide content in the paint led to increased reaction with the resinic acids , demonstrated by the residual acidity . For example , in paints 10 ...
... oxidation of cuprous oxide . As was observed during extender dispersion , increased cuprous oxide content in the paint led to increased reaction with the resinic acids , demonstrated by the residual acidity . For example , in paints 10 ...
Page 247
... oxide films ) diffusing from a surface is proportional to the square root of time / 10,11 / . Linear oxide growth with the square root of time is also indicative of passive , protective film formation / 12 / . The graph shows that the ...
... oxide films ) diffusing from a surface is proportional to the square root of time / 10,11 / . Linear oxide growth with the square root of time is also indicative of passive , protective film formation / 12 / . The graph shows that the ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90