Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 17
Page 395
... open circuit potential of zirconium in HNO3 moves toward the noble direction . However , as shown in Fig . 1 , the open circuit potentials of zirconium electrode in HF - containing 90 % HNO3 solutions move toward the active direction ...
... open circuit potential of zirconium in HNO3 moves toward the noble direction . However , as shown in Fig . 1 , the open circuit potentials of zirconium electrode in HF - containing 90 % HNO3 solutions move toward the active direction ...
Page 405
... open - circuit potential of the samples containing Cu [ -200mV ( SCE ) ] is similar to that of wrought plate stainless steel of type AISI 316 / 2 / . The weight loss of the samples containing Cu during the immersion test was negligible ...
... open - circuit potential of the samples containing Cu [ -200mV ( SCE ) ] is similar to that of wrought plate stainless steel of type AISI 316 / 2 / . The weight loss of the samples containing Cu during the immersion test was negligible ...
Page 406
... open - circuit potentials are observed . This behaviour could be related to selective anodic dissolution of the active surface followed by local enrichment of the noble alloying element , / 15 , 16 / being probably Cu . During the ...
... open - circuit potentials are observed . This behaviour could be related to selective anodic dissolution of the active surface followed by local enrichment of the noble alloying element , / 15 , 16 / being probably Cu . During the ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90