Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 47
Page 410
... immersion test and the open circuit potential was in the passive range . From the presented results and other ... immersion up to total loss . The corrosion processes were followed by hydrogen evolution . Samples containing Pd addition ...
... immersion test and the open circuit potential was in the passive range . From the presented results and other ... immersion up to total loss . The corrosion processes were followed by hydrogen evolution . Samples containing Pd addition ...
Page 89
... immersion tests ( raft and ships hull , dry film thickness , immersion time , neutralization chemical reactions between sea water cations and remaining acidic components of binder ) and , finally , characteristics of aged paints after ...
... immersion tests ( raft and ships hull , dry film thickness , immersion time , neutralization chemical reactions between sea water cations and remaining acidic components of binder ) and , finally , characteristics of aged paints after ...
Page 135
... immersion , forming resinates . with the divalent cations , which remain in the film during long immersion periods . After those periods , free resinic acids were practically absent in the film and binder dissolution was a consequence ...
... immersion , forming resinates . with the divalent cations , which remain in the film during long immersion periods . After those periods , free resinic acids were practically absent in the film and binder dissolution was a consequence ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90