Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 64
Page 107
... higher temperatures ( up to 90 ° C ) further increase is necessary to ensure full protection / 42 / . Studies of film growth were not made and no light could be thrown on the mechanism of inhibition . Leckie and Uhlig / 62 / observed ...
... higher temperatures ( up to 90 ° C ) further increase is necessary to ensure full protection / 42 / . Studies of film growth were not made and no light could be thrown on the mechanism of inhibition . Leckie and Uhlig / 62 / observed ...
Page 319
... higher one goes in % CI , the higher the alloy required to serve effectively . Claims for resistance in furnace grade or reagent grade phosphoric acid are not relevant for the WPA industry . Many of the specialty alloys particularly ...
... higher one goes in % CI , the higher the alloy required to serve effectively . Claims for resistance in furnace grade or reagent grade phosphoric acid are not relevant for the WPA industry . Many of the specialty alloys particularly ...
Page 333
... higher . The comparable priced Uranus UB6 had a 57 % higher rate than that found for CED . The less expensive 316 stainless steel was 1657 % higher . - Pitting and crevice corrosion No pitting was observed on CED - H3PO4 systems ...
... higher . The comparable priced Uranus UB6 had a 57 % higher rate than that found for CED . The less expensive 316 stainless steel was 1657 % higher . - Pitting and crevice corrosion No pitting was observed on CED - H3PO4 systems ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90