... fluoride content produced a more severe environment , even in the presence of flyash . Crevice pits which initiated in 30 days , failed to propagate with additional exposure to 90 days ; however , the degree of initiation increased . 1 ...
... fluoride content produced a more severe environment , even in the presence of flyash . Crevice pits which initiated in 30 days , failed to propagate with additional exposure to 90 days ; however , the degree of initiation increased . 1 ...
Page 373
... Fluoride Content In runs 5 to 7 , with a 50,000 ppm chloride ( derived from Ca , Na and Mg salts ) environment , the absorber slurry fluoride content was varied as follows : In run 5 no fluoride was added . In runs 6 and 7 , 300 ppm ...
... Fluoride Content In runs 5 to 7 , with a 50,000 ppm chloride ( derived from Ca , Na and Mg salts ) environment , the absorber slurry fluoride content was varied as follows : In run 5 no fluoride was added . In runs 6 and 7 , 300 ppm ...
Page 395
... fluoride complexes . Fluoride ions can be much more efficiently complexed by zirconium sponge than by solid zirconium . In a fluoride - containing solution , the presence of zirconium ions or more active zirconium in solution will ...
... fluoride complexes . Fluoride ions can be much more efficiently complexed by zirconium sponge than by solid zirconium . In a fluoride - containing solution , the presence of zirconium ions or more active zirconium in solution will ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90