... environment temperature and concentrations for a specified environment or 3 ) by tabular listing of corrosion rate data for a specified material in a corrosive environment as a function of temperature and concentration . CORSUR provides ...
... environment temperature and concentrations for a specified environment or 3 ) by tabular listing of corrosion rate data for a specified material in a corrosive environment as a function of temperature and concentration . CORSUR provides ...
Page 360
... environmental effects on localized corrosion propagation of each alloy . Increasing environmental chloride and / or fluoride content produced a more severe environment , even in the presence of flyash . Crevice pits which initiated in ...
... environmental effects on localized corrosion propagation of each alloy . Increasing environmental chloride and / or fluoride content produced a more severe environment , even in the presence of flyash . Crevice pits which initiated in ...
Page 373
... environmental chloride content , major attack only occurred in the 100,000 ppm chloride environment . See run 4 in Table 6. The reason for the unexpected behavior of alloy 625 is not clearly discernible . 3.1 Effect of Environmental ...
... environmental chloride content , major attack only occurred in the 100,000 ppm chloride environment . See run 4 in Table 6. The reason for the unexpected behavior of alloy 625 is not clearly discernible . 3.1 Effect of Environmental ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90