Table 2 shows the values of the two corrosion densities , le and I. , electrochemical and gravimetric respectively , of the polarization resistance , Ro , and of the inhibitor effectiveness ( I.E. ) based on R , and I g ' It should be ...
Table 2 shows the values of the two corrosion densities , le and I. , electrochemical and gravimetric respectively , of the polarization resistance , Ro , and of the inhibitor effectiveness ( I.E. ) based on R , and I g ' It should be ...
Page 52
With regard to the corrosion current density , I. , derived from electrochemical measurements , it yields very satisfactory results in the case of inhibitor B , while in the other three cases its reproduction of the real trend of the ...
With regard to the corrosion current density , I. , derived from electrochemical measurements , it yields very satisfactory results in the case of inhibitor B , while in the other three cases its reproduction of the real trend of the ...
Page 261
Electrochemical Mechanism The magnetite film on the inner surface of the steam generator tubes is never completely impermeable . In fact , it presents some microporosities which favour contact between the cleaning solution and the base ...
Electrochemical Mechanism The magnetite film on the inner surface of the steam generator tubes is never completely impermeable . In fact , it presents some microporosities which favour contact between the cleaning solution and the base ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy aluminum analysis anodic application base changes chemical cleaning coatings combination compared composition concentration conclusion considered containing copper corrosion Corrosion Control curve density deposits described determine direct effect electrochemical electron Engineering environment equipment evaluation example experimental expert system factor field Figure function given higher important increase industry inhibitor ions Israel knowledge layer less limited materials measurements mechanical metal method observed obtained operation organic oxide paint passivation performance plant plating polarization possible potential practical present problems properties protection Radioactive Tracer reduce reference reported resistance REVIEWS rules runs rust samples selection shown shows solution specific specimen stainless steel standard structure surface Table technique Technology temperature tube values welding