Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 25
Page 373
... crevice pit depth also increased with increasing environmental chloride content . While SS304 did not significantly crevice corrode , it did suffer severe general corrosion . See Figure 2 . Also seen in Figure 4 , alloy 904L appears to ...
... crevice pit depth also increased with increasing environmental chloride content . While SS304 did not significantly crevice corrode , it did suffer severe general corrosion . See Figure 2 . Also seen in Figure 4 , alloy 904L appears to ...
Page 376
Crevice Pit Depth , respectively , plotted versus Environmental Fluoride Content in the outlet duct . Generally , both bold surface and crevice pit depth increased with increasing environmental fluoride content . No. consistent effect ...
Crevice Pit Depth , respectively , plotted versus Environmental Fluoride Content in the outlet duct . Generally , both bold surface and crevice pit depth increased with increasing environmental fluoride content . No. consistent effect ...
Page 383
... crevice attack in the outlet ducting zone also increased with increasing chloride content , except for SS304 which suffered severe general corrosion . Alloys G , 625 and SS316 displayed a greater rate of increase than alloys 904L and C ...
... crevice attack in the outlet ducting zone also increased with increasing chloride content , except for SS304 which suffered severe general corrosion . Alloys G , 625 and SS316 displayed a greater rate of increase than alloys 904L and C ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90