Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 22
Page 334
... corrosion fatigue . As mentioned above for stress corrosion , however , a more reliable measure of corrosion fatigue susceptibility require the use of fracture mechanics test techniques . Erosion / corrosion and impingement attack - The ...
... corrosion fatigue . As mentioned above for stress corrosion , however , a more reliable measure of corrosion fatigue susceptibility require the use of fracture mechanics test techniques . Erosion / corrosion and impingement attack - The ...
Page 23
... corrosion fatigue cracks on this surface contained microscopic spikes of lead along the core of the cracks ( Figure 16 ) . Pb Lead Channeling Along Corrosion Fatigue Crack Fig . 16 700x Backscatter electron image from a SEM . Ruptures ...
... corrosion fatigue cracks on this surface contained microscopic spikes of lead along the core of the cracks ( Figure 16 ) . Pb Lead Channeling Along Corrosion Fatigue Crack Fig . 16 700x Backscatter electron image from a SEM . Ruptures ...
Page 24
... Corrosion Fatigue Crack Fig . 17 500x Lead running from tip of corrosion fatigue crack - backscatter electron image . Figure 18 is an EDS spectrum of the material within the cracks showing the presence of both lead and antimony . Lead ...
... Corrosion Fatigue Crack Fig . 17 500x Lead running from tip of corrosion fatigue crack - backscatter electron image . Figure 18 is an EDS spectrum of the material within the cracks showing the presence of both lead and antimony . Lead ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90