Page 42
The tin - lead solder was applied to the defect after the area had been cleaned , zincated and brush coated with nickel - copper alloy ( Ref . 6 ) . This is very important , because in modern cars , radiators , coolers and air ...
The tin - lead solder was applied to the defect after the area had been cleaned , zincated and brush coated with nickel - copper alloy ( Ref . 6 ) . This is very important , because in modern cars , radiators , coolers and air ...
Page 120
The analysis of the commercial pigment employed in the experiences performed by the authors showed that the content of metallic copper ( Cu9 and Cu ( II ) , 24 hours after preparation , is low and of similar magnitude : 0.03 and 0.04 ...
The analysis of the commercial pigment employed in the experiences performed by the authors showed that the content of metallic copper ( Cu9 and Cu ( II ) , 24 hours after preparation , is low and of similar magnitude : 0.03 and 0.04 ...
Page 186
Godard / 35 / studied corrosion of copper and aluminum by AC in water . For AC density of 24 A / m2 , weight loss for aluminum and copper was 27 % and 1 % respectively of the theoretical values calculated for the anodic portion .
Godard / 35 / studied corrosion of copper and aluminum by AC in water . For AC density of 24 A / m2 , weight loss for aluminum and copper was 27 % and 1 % respectively of the theoretical values calculated for the anodic portion .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy aluminum analysis anodic application base changes chemical cleaning coatings combination compared composition concentration conclusion considered containing copper corrosion Corrosion Control curve density deposits described determine direct effect electrochemical electron Engineering environment equipment evaluation example experimental expert system factor field Figure function given higher important increase industry inhibitor ions Israel knowledge layer less limited materials measurements mechanical metal method observed obtained operation organic oxide paint passivation performance plant plating polarization possible potential practical present problems properties protection Radioactive Tracer reduce reference reported resistance REVIEWS rules runs rust samples selection shown shows solution specific specimen stainless steel standard structure surface Table technique Technology temperature tube values welding