Page 405
The potential of the samples containing Cu at various concentrations reaches a value of about + 200mV ( SCE ) as compared to – 250mV ( SCE ) for the hot pressed sintered stainless steel . Hydrogen evolution is observed at potential ...
The potential of the samples containing Cu at various concentrations reaches a value of about + 200mV ( SCE ) as compared to – 250mV ( SCE ) for the hot pressed sintered stainless steel . Hydrogen evolution is observed at potential ...
Page 408
Behavior of Sintered Stainless Steel containing Ni ( + 200mV ( SCE ) ] is similar to that of wrought plate stainless steel of type AISI 316 / 1 / . The weight loss of the samples containing Ni during the immersion test was negligible .
Behavior of Sintered Stainless Steel containing Ni ( + 200mV ( SCE ) ] is similar to that of wrought plate stainless steel of type AISI 316 / 1 / . The weight loss of the samples containing Ni during the immersion test was negligible .
Page 410
The critical and passivation current densities of the samples containing various Ni concentrations are similar to wrought plate stainless steel . The potentiodynamic behaviour of hot pressed and sintered stainless steel demonstrates ...
The critical and passivation current densities of the samples containing various Ni concentrations are similar to wrought plate stainless steel . The potentiodynamic behaviour of hot pressed and sintered stainless steel demonstrates ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy aluminum analysis anodic application base changes chemical cleaning coatings combination compared composition concentration conclusion considered containing copper corrosion Corrosion Control curve density deposits described determine direct effect electrochemical electron Engineering environment equipment evaluation example experimental expert system factor field Figure function given higher important increase industry inhibitor ions Israel knowledge layer less limited materials measurements mechanical metal method observed obtained operation organic oxide paint passivation performance plant plating polarization possible potential practical present problems properties protection Radioactive Tracer reduce reference reported resistance REVIEWS rules runs rust samples selection shown shows solution specific specimen stainless steel standard structure surface Table technique Technology temperature tube values welding