Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 82
Page 405
... containing Cu at various concentrations reaches a value of about + 200mV ( SCE ) as compared to -250mV ( SCE ) for the hot pressed sintered stainless steel . Hydrogen evolution is observed at potential lower than -200mV ( SCE ) ...
... containing Cu at various concentrations reaches a value of about + 200mV ( SCE ) as compared to -250mV ( SCE ) for the hot pressed sintered stainless steel . Hydrogen evolution is observed at potential lower than -200mV ( SCE ) ...
Page 408
... containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) . During the exposure to IN H2SO4 higher ...
... containing Ni during the immersion test was negligible . In the first stages , the value of the open circuit potential of the samples containing 1 and 5wt % Ni are lower than + 200mV ( SCE ) . During the exposure to IN H2SO4 higher ...
Page 410
... containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples containing Ni ...
... containing Ni . Lower critical and passivation current densities were observed as compared to the samples sintered for 2h , and as compared to the hot pressed sintered stainless steel . It should be emphasized that samples containing Ni ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90