... considered here . Only those coating methods in which the formation of a functional alloy coating is controlled by interdiffusivity of the coating and substrate metals are considered here ( Fig . 8 ) . Diffusion methods have basically ...
... considered here . Only those coating methods in which the formation of a functional alloy coating is controlled by interdiffusivity of the coating and substrate metals are considered here ( Fig . 8 ) . Diffusion methods have basically ...
Page 268
... considered satisfactory practically coincides with the interval within which ( 13 ) is valid . Thus , under these circumstances , expression ( 14 ) reduces significantly the influence of random errors in the polarization curve considered ...
... considered satisfactory practically coincides with the interval within which ( 13 ) is valid . Thus , under these circumstances , expression ( 14 ) reduces significantly the influence of random errors in the polarization curve considered ...
Page 285
... considered were pitting , erosion - corrosion and dealloying . Electrochemical techniques were used and different experi- ments and tests were designed to simulate operative conditions . According to the results of this study , Al ...
... considered were pitting , erosion - corrosion and dealloying . Electrochemical techniques were used and different experi- ments and tests were designed to simulate operative conditions . According to the results of this study , Al ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90