Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 72
Page 103
... concentration of chromate increased . Although the concentration required to inhibit corrosion was independent of the area of the surface protected , the rate of consumption was a function of the metal area and the original concentration ...
... concentration of chromate increased . Although the concentration required to inhibit corrosion was independent of the area of the surface protected , the rate of consumption was a function of the metal area and the original concentration ...
Page 40
... concentration is lower than the recommended one , so that the solution aggressiveness towards the base metal can become very high . A negative characteristic of all inhibitors , whether pure compounds or commercial products , is that ...
... concentration is lower than the recommended one , so that the solution aggressiveness towards the base metal can become very high . A negative characteristic of all inhibitors , whether pure compounds or commercial products , is that ...
Page 318
... concentration was measured with a specific electrode . The colloid concentration was determined by turbidimetry in a Beckman 34 Spectrophotometer at a 420 nm wave- length . The results are shown in Figs . 22 , 23 , and 24 . After 300 ...
... concentration was measured with a specific electrode . The colloid concentration was determined by turbidimetry in a Beckman 34 Spectrophotometer at a 420 nm wave- length . The results are shown in Figs . 22 , 23 , and 24 . After 300 ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90