Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 53
Page 104
... chloride on inhibition by chromates at various temperatures was examined by Roetheli & Cox / 60 / , who found that larger quantities of chromates are needed with increase of either salt concentration or temperature . Darrin also ...
... chloride on inhibition by chromates at various temperatures was examined by Roetheli & Cox / 60 / , who found that larger quantities of chromates are needed with increase of either salt concentration or temperature . Darrin also ...
Page 369
... Chloride Content for the outlet ducting Zone F. As seen in Figure 2 , the corrosion rate of alloys SS304 and SS316 increased with increasing environmental chloride content . Alloys G. 904L , 625 and C - 4 exhibited very low corrosion ...
... Chloride Content for the outlet ducting Zone F. As seen in Figure 2 , the corrosion rate of alloys SS304 and SS316 increased with increasing environmental chloride content . Alloys G. 904L , 625 and C - 4 exhibited very low corrosion ...
Page 383
... chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with alloy ...
... chlorides increasing from 10,000 to 100,000 ppm . 2. Maximum depth of bold surface pitting in the outlet ducting zone increased with increasing slurry chloride for all the alloys except alloy C - 4 . The highest increase was with alloy ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90