Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 55
Page 411
... anodic direction up to + 1250mV ( SCE ) and then to the cathodic direction back to the initial potential . These measurments show the cathodic - anodic transition in each direction of scanning . Effective anodic passivation is not ...
... anodic direction up to + 1250mV ( SCE ) and then to the cathodic direction back to the initial potential . These measurments show the cathodic - anodic transition in each direction of scanning . Effective anodic passivation is not ...
Page 413
... anodic passivation and show high anodic - cathodic transition potential at about 375mV ( SCE ) . The results presented show that although the Pd addition slightly improves the pores morphology , the anodic passivation is dependent on ...
... anodic passivation and show high anodic - cathodic transition potential at about 375mV ( SCE ) . The results presented show that although the Pd addition slightly improves the pores morphology , the anodic passivation is dependent on ...
Page 295
... Anodic curves for Cu - Ni 70/30 . anodic respect to the Ecorr in the polished condition , but it moves to 180 mV respect to the E in the aged condition . In the presence of corr sulphide the pitting potential for each condition is ...
... Anodic curves for Cu - Ni 70/30 . anodic respect to the Ecorr in the polished condition , but it moves to 180 mV respect to the E in the aged condition . In the presence of corr sulphide the pitting potential for each condition is ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90