Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 54
Page 411
... anodic direction up to + 1250mV ( SCE ) and then to the cathodic direction back to the initial potential . These measurments show the cathodic - anodic transition in each direction of scanning . Effective anodic passivation is not ...
... anodic direction up to + 1250mV ( SCE ) and then to the cathodic direction back to the initial potential . These measurments show the cathodic - anodic transition in each direction of scanning . Effective anodic passivation is not ...
Page 413
... anodic passivation and show high anodic - cathodic transition potential at about 375mV ( SCE ) . The results presented show that although the Pd addition slightly improves the pores morphology , the anodic passivation is dependent on ...
... anodic passivation and show high anodic - cathodic transition potential at about 375mV ( SCE ) . The results presented show that although the Pd addition slightly improves the pores morphology , the anodic passivation is dependent on ...
Page 295
... Anodic curves for Cu - Ni 70/30 . corr anodic respect to the Ecorr in the polished condition , but it moves to 180 mV respect to the E in the aged condition . In the presence of sulphide the pitting potential for each condition is ...
... Anodic curves for Cu - Ni 70/30 . corr anodic respect to the Ecorr in the polished condition , but it moves to 180 mV respect to the E in the aged condition . In the presence of sulphide the pitting potential for each condition is ...
Contents
ABSTRACT | 36 |
COATINGS FOR BRAZING the wett | 45 |
CONTENTS | 96 |
Copyright | |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anodic antifouling Antifouling Paints application Artificial Intelligence Austenitic behaviour boiler brazing carbon cathodic protection chemical chloride chromate coatings composition concentration copper CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS cupronickels cuprous oxide current density deposits dissolution effect electrochemical electrode electroplating environment evaluation example experimental expert system Fe+2 Hastelloy HNO3 hydrazine immersion increase industry inhibition inhibitor interface ion implantation ions Israel knowledge base laboratory layer magnetite materials selection measurements mechanical metal method MYCIN NACE obtained oxide film oxygen paper parameters passivation performance plant plating polarization curves polymer potential potentiostat Power Stations Prof properties resinic acids rules rust samples Schorr sintered slurry soldering solution specimens stainless steel steam structure substrate surface Table techniques Technology temperature thermal thickness tubes values welding zirconium