Page 373
As seen in Tables 5 and 6 , alloy C - 276 was only tested in runs 2 and 3 in Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least ...
As seen in Tables 5 and 6 , alloy C - 276 was only tested in runs 2 and 3 in Zone B and in run 4 in Zone F. In these cases , alloy C - 276 exhibited excellent corrosion resistance . As seen in Figure 4 , except for alloy 304 , the least ...
Page 376
No consistent effect of flyash ( added to the slurry ) on alloy corrosion resistance was discernible . The alloys ranked as to increasing localized corrosion resistance as follows : alloy G , alloy 904L , SS317LM , SS316 , alloy G - 3 ...
No consistent effect of flyash ( added to the slurry ) on alloy corrosion resistance was discernible . The alloys ranked as to increasing localized corrosion resistance as follows : alloy G , alloy 904L , SS317LM , SS316 , alloy G - 3 ...
Page 66
ONLY ) SEAL WELD CMFE ON STEEL WELC ALLOY CAFE ON STEEL BATTEN STRIP OVERLAP Fig . 4 . Typical clad plate con struction joint designs . The batten strip configuration has a carbon steel border visible on four sides when viewed from the ...
ONLY ) SEAL WELD CMFE ON STEEL WELC ALLOY CAFE ON STEEL BATTEN STRIP OVERLAP Fig . 4 . Typical clad plate con struction joint designs . The batten strip configuration has a carbon steel border visible on four sides when viewed from the ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy aluminum analysis anodic application base changes chemical cleaning coatings combination compared composition concentration conclusion considered containing copper corrosion Corrosion Control curve density deposits described determine direct effect electrochemical electron Engineering environment equipment evaluation example experimental expert system factor field Figure function given higher important increase industry inhibitor ions Israel knowledge layer less limited materials measurements mechanical metal method observed obtained operation organic oxide paint passivation performance plant plating polarization possible potential practical present problems properties protection Radioactive Tracer reduce reference reported resistance REVIEWS rules runs rust samples selection shown shows solution specific specimen stainless steel standard structure surface Table technique Technology temperature tube values welding