Corrosion Reviews, Volumes 7-8Scientific Publications Division, Freund Publishing House, 1987 |
From inside the book
Results 1-3 of 93
Page 373
... alloy 904L appears to exhibit better localized corrosion resistance than higher molybdenum alloys such as alloy 625 . However , alloy 904L suffered far greater bold surface pit penetration , as seen in Figure 3 , which may have ...
... alloy 904L appears to exhibit better localized corrosion resistance than higher molybdenum alloys such as alloy 625 . However , alloy 904L suffered far greater bold surface pit penetration , as seen in Figure 3 , which may have ...
Page 376
... alloy corrosion resistance was discernible . The alloys ranked as to increasing localized corrosion resistance as follows : alloy G , alloy 904L , SS317LM , SS316 , alloy G - 3 similar to alloy 625 , alloy C - 276 . Alloy 625 was more ...
... alloy corrosion resistance was discernible . The alloys ranked as to increasing localized corrosion resistance as follows : alloy G , alloy 904L , SS317LM , SS316 , alloy G - 3 similar to alloy 625 , alloy C - 276 . Alloy 625 was more ...
Page 63
... alloy 625 and titanium shows that titanium , which has a density of 4.5 g / cc , will cover almost twice the area of alloy 625 , which has a density of 8.4 g / cc . Based on only the material cost , therefore , titanium is nearly twice ...
... alloy 625 and titanium shows that titanium , which has a density of 4.5 g / cc , will cover almost twice the area of alloy 625 , which has a density of 8.4 g / cc . Based on only the material cost , therefore , titanium is nearly twice ...
Contents
ABSTRACT | 36 |
COATINGS FOR BRAZING the wett | 45 |
CONTENTS | 96 |
Copyright | |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anodic antifouling Antifouling Paints application Artificial Intelligence Austenitic behaviour boiler brazing carbon cathodic protection chemical chloride chromate coatings composition concentration copper CorDorCD Corrosion Control Corrosion Engineers corrosion problems corrosion rate corrosion resistance CORROSION REVIEWS cupronickels cuprous oxide current density deposits dissolution effect electrochemical electrode electroplating environment evaluation example experimental expert system Fe+2 Hastelloy HNO3 hydrazine immersion increase industry inhibition inhibitor interface ion implantation ions Israel knowledge base laboratory layer magnetite materials selection measurements mechanical metal method MYCIN NACE obtained oxide film oxygen paper parameters passivation performance plant plating polarization curves polymer potential potentiostat Power Stations Prof properties resinic acids rules rust samples Schorr sintered slurry soldering solution specimens stainless steel steam structure substrate surface Table techniques Technology temperature thermal thickness tubes values welding zirconium