Table 6 shows that the addition of 200ppm HF with or without 800 ppm zirconium sponge to 90 % HNO3 eliminates zirconium's SCC susceptibility . The addition of 800 ppm zirconium sponge only produced little changes .
Table 6 shows that the addition of 200ppm HF with or without 800 ppm zirconium sponge to 90 % HNO3 eliminates zirconium's SCC susceptibility . The addition of 800 ppm zirconium sponge only produced little changes .
Page 403
Sn addition improves the corrosion resistance of sintered austenitic stainless steel 13 / mainly by decreasing the density of interconnected open pores . Cr depletion processes due to carbides or other phases precipitation such as Cr2N ...
Sn addition improves the corrosion resistance of sintered austenitic stainless steel 13 / mainly by decreasing the density of interconnected open pores . Cr depletion processes due to carbides or other phases precipitation such as Cr2N ...
Page 410
The Pd addition up to 5Wt % reacts with the austenitic matrix to form a solid solution . X - Ray diffraction revealed the existence of carbide phases such as M23Co and M3C , after the sintering process . Pd containing phases were not ...
The Pd addition up to 5Wt % reacts with the austenitic matrix to form a solid solution . X - Ray diffraction revealed the existence of carbide phases such as M23Co and M3C , after the sintering process . Pd containing phases were not ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Other editions - View all
Common terms and phrases
acid activity addition alloy aluminum analysis anodic application base changes chemical cleaning coatings combination compared composition concentration conclusion considered containing copper corrosion Corrosion Control curve density deposits described determine direct effect electrochemical electron Engineering environment equipment evaluation example experimental expert system factor field Figure function given higher important increase industry inhibitor ions Israel knowledge layer less limited materials measurements mechanical metal method observed obtained operation organic oxide paint passivation performance plant plating polarization possible potential practical present problems properties protection Radioactive Tracer reduce reference reported resistance REVIEWS rules runs rust samples selection shown shows solution specific specimen stainless steel standard structure surface Table technique Technology temperature tube values welding