Page 396
... addition of 800ppm zirconium sponge only produced little changes . The addition of zirconium sponge into HF - containing HNO3 was solely for preventing the high corrosion rate of the test specimen of zirconium . Furthermore ...
... addition of 800ppm zirconium sponge only produced little changes . The addition of zirconium sponge into HF - containing HNO3 was solely for preventing the high corrosion rate of the test specimen of zirconium . Furthermore ...
Page 403
... addition improves the corrosion resistance of sintered austenitic stainless steel / 3 / mainly by decreasing the density of interconnected open pores . Cr depletion processes due to carbides or other phases precipitation such as Cr2N ...
... addition improves the corrosion resistance of sintered austenitic stainless steel / 3 / mainly by decreasing the density of interconnected open pores . Cr depletion processes due to carbides or other phases precipitation such as Cr2N ...
Page 410
... addition is not sufficient for self passivation . 4.3 . Effect of Pd Microstructure of samples sintered at 1150 ° C for 48h is presented in Fig . 6. It can be seen that pore shape and dimension of samples containing Pd are slightly ...
... addition is not sufficient for self passivation . 4.3 . Effect of Pd Microstructure of samples sintered at 1150 ° C for 48h is presented in Fig . 6. It can be seen that pore shape and dimension of samples containing Pd are slightly ...
Other editions - View all
Common terms and phrases
acid addition alloy aluminum anodic Antifouling Paints application austenitic base Beatriz del Amo behaviour binder boiler carbon Catalyzed Hydrazine cathodic protection chemical chloride coatings concentration conductors copper Corrosion Control Corrosion Engineers corrosion rate corrosion resistance crack cuprous oxide current density deposits dispersion dissolution rate effect electrical Electrical Conductors electrochemical electron environments evaluation expert system film fluoride Hastelloy HNO3 hot pressed hydrazine hydropower immersion increase industrial inhibitor ions Israel layer materials metal NACE Offshore Platforms open circuit oxygen oxygen scavengers Paints for Ships passivation performance pigment plant plate polarization curves Power Stations problems Prof Puerto Belgrano Rascio resinates resinic acids rosin rupture rust sea water sintered stainless steel slurry soluble solution specimens strain rate stress stress corrosion cracking structure substrate sulfite Table technique Technology temperature toxicant tube values weld zinc zirconium zirconium in 90