Natural Weathering of Mineral Stabilized Asphalt Coatings on Organic Felt |
From inside the book
Results 1-5 of 5
Page
Aluminum - base panels 2.3 . Materials . Mineral matter . b . Asphalts Saturated felts . d . Aluminum panels . Granules 2.4 . Specimen preparation Smooth - surface , felt - base specimens . b . Granule - surfaced , felt - base specimens ...
Aluminum - base panels 2.3 . Materials . Mineral matter . b . Asphalts Saturated felts . d . Aluminum panels . Granules 2.4 . Specimen preparation Smooth - surface , felt - base specimens . b . Granule - surfaced , felt - base specimens ...
Page 2
It consisted of the coating on 234- X 6 - in aluminum panels . The results of these tests were reported earlier ( 3 ) . E. Embedding rolls . F. Belt drive for pulling canvas belt through the machine . c . Back - Coater 2.2 .
It consisted of the coating on 234- X 6 - in aluminum panels . The results of these tests were reported earlier ( 3 ) . E. Embedding rolls . F. Belt drive for pulling canvas belt through the machine . c . Back - Coater 2.2 .
Page 5
After about 30 s , the panel was removed from between the sheets of Kraft paper and placed in a water bath at room ... When the required number of acceptable panels had been prepared , the hot coating was ladled from the melting bath to ...
After about 30 s , the panel was removed from between the sheets of Kraft paper and placed in a water bath at room ... When the required number of acceptable panels had been prepared , the hot coating was ladled from the melting bath to ...
Page 6
When cool , the thickness of the coated panel was measured . In a normal run the felt panel was fastened with masking tape to the Kraft paper on the hot plate . About one and a half times the required coating was distributed over the ...
When cool , the thickness of the coated panel was measured . In a normal run the felt panel was fastened with masking tape to the Kraft paper on the hot plate . About one and a half times the required coating was distributed over the ...
Page 10
The dots represent the average durability of four specimens on aluminum panels exposed in the weatherometers and the bars represent the average durability of two felt - base specimens exposed outdoors . Based on those specimens exposed ...
The dots represent the average durability of four specimens on aluminum panels exposed in the weatherometers and the bars represent the average durability of two felt - base specimens exposed outdoors . Based on those specimens exposed ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Common terms and phrases
60 percent aluminum aluminum-base specimens appearance Applied asphalt coatings ASTM base Black Slate 25 blistering Blue Black Slate Building Building Science Series Bureau of Standards California asphalt Cement Center cents Characteristics Clay Column COMMERCE Composition Coating thickness concentrations consists containing corresponding cracking criteria deterioration differences direction divisions doctor bar Dolomite durability early effects exposed exposure failed failure felt-base specimens FIGURE Fly Ash Government granule-surfaced specimens granules heated industry instances Institute Loss on ignition losses machine materials measurement method Mica Mid-Continent asphalt mils mineral additives Months Ratio Months National Bureau observed Office panel passed performances period physical prepared produced Properties provides Ratio Months Ratio reference reported Research Retained rolls roofing saturated felt sheets shingle Silica smooth smooth-surface smooth-surface specimens spalling surface tabs technical Technology temperature tests three asphalts type of specimen Venezuela asphalt Washington weather
Bibliographic information
| Title | Natural Weathering of Mineral Stabilized Asphalt Coatings on Organic Felt Volume 24 of Building science series, United States National Bureau of Standards Volume 24 of National Bureau of Standards building science series |
| Author | Sidney H. Greenfeld |
| Publisher | U.S. National Bureau of Standards, 1969 |
| Original from | the University of Michigan |
| Digitized | 18 Aug 2006 |
| Length | 15 pages |
| Export Citation | BiBTeX EndNote RefMan |