Natural Weathering of Mineral Stabilized Asphalt Coatings on Organic FeltU.S. National Bureau of Standards, 1969 - 15 pages Sixteen years of outdoor weathering of laboratory-prepared smooth-surface and mineral-surfaced, felt-base roofing specimens has provided information on the effects of mineral additives on the durability of coating-grade roofing asphalts. Six finely divided mineral additives (blue black slate, clay, dolomite, fly ash, mica, and silica) were evaluated at concentrations up to 60 percent in California, Mid Continent and Venezuela asphalts. The mineral-surfaced specimens are all performing satisfactorily, and show only minor degrees of degradation. Of the smooth-surfaced specimens, the Mid-Continent asphalt performed the best and the California asphalt the poorest. The mica and blue black slate increased the durabilities of all three asphalts at all concentrations and two coating thicknesses. Fly ash, clay, dolomite, and silica were beneficial in some combinations, but had little effect in others. In general, these early results from outdoor exposure tend to corroborate the results obtained on these coatings exposed in weatherometers. (Author). |
From inside the book
Results 1-5 of 6
Page 3
... Loss on ignition at 1000 ° F . Loss on ignition at 1800 ° F . Moisture- Solubility . Free alkali .m2 / g .. 2.94 2.64 2.87 2.62 3.01 2.68 1.0 27.2 2.0 2.0 2.7 2.5 lb / 100 lb. 29.5 63.9 19.4 30.0 97.2 19.5 lb / 100 lb .. 32.7 36.4 18.5 ...
... Loss on ignition at 1000 ° F . Loss on ignition at 1800 ° F . Moisture- Solubility . Free alkali .m2 / g .. 2.94 2.64 2.87 2.62 3.01 2.68 1.0 27.2 2.0 2.0 2.7 2.5 lb / 100 lb. 29.5 63.9 19.4 30.0 97.2 19.5 lb / 100 lb .. 32.7 36.4 18.5 ...
Page 4
... Loss on heating , ' . - % -- 0.22 0.03 0.10 Penetration at 77 ° F ( 25 ° C ) after heating , 0.1 .. mm . 17 17 14 Specific gravity at 77 ° F ( 25 ° C ) 1.015 0.999 1.018 Viscosity , cP at 400 ° F ( 204 ° C ) 280 420 375 Viscosity , cP ...
... Loss on heating , ' . - % -- 0.22 0.03 0.10 Penetration at 77 ° F ( 25 ° C ) after heating , 0.1 .. mm . 17 17 14 Specific gravity at 77 ° F ( 25 ° C ) 1.015 0.999 1.018 Viscosity , cP at 400 ° F ( 204 ° C ) 280 420 375 Viscosity , cP ...
Page 5
... loss . 80 percent . 6 lb / ton ( 3 g / kg ) . Particle Size ( Tyler ) Sieve No. Percent Retained on 10 0.7 Retained on 14 33.9 Retained on 20 36.0 Retained on 28 21.6 Retained on 35 7.2 Passing 35 0.5 Granules were oiled with 5 lb per ...
... loss . 80 percent . 6 lb / ton ( 3 g / kg ) . Particle Size ( Tyler ) Sieve No. Percent Retained on 10 0.7 Retained on 14 33.9 Retained on 20 36.0 Retained on 28 21.6 Retained on 35 7.2 Passing 35 0.5 Granules were oiled with 5 lb per ...
Page 7
... losses of granules in the few specimens in which poor granule adhesion was measured prior to exposure . After about ... loss in 49 grid areas ( 50 % ) or spalls in 25 grid areas ( 25 % ) . Cracks in 30 grid areas ( 50 % ) few of the ...
... losses of granules in the few specimens in which poor granule adhesion was measured prior to exposure . After about ... loss in 49 grid areas ( 50 % ) or spalls in 25 grid areas ( 25 % ) . Cracks in 30 grid areas ( 50 % ) few of the ...
Page 10
... losses of granules early during their exposure . The California specimens containing clay passed the test marginally . They , also , lost some granules early during exposure . However , none of these specimens has failed by the ...
... losses of granules early during their exposure . The California specimens containing clay passed the test marginally . They , also , lost some granules early during exposure . However , none of these specimens has failed by the ...
Common terms and phrases
15 cents 60 percent silica aluminum-base specimens ARIB ASTM method automatic data processing back-coated Black Slate 25 blistering Blue Black Slate Building Science Series Bureau of Standards California asphalt Cement and Concrete Coating composition Thickness Coating thickness Composition Column 1 Column Composition Coating thickness Concrete Properties cracking and spalling doctor bar Dolomite 25 35 embedding rolls felt-base specimens Fly Ash 25 Fly Ash 50 granule-surfaced specimens Greenfeld increased the durability Institute for Applied Interrelations Between Cement Isopropyl alcohol Kraft paper Lake Erie Loss on ignition losses of granules Mica Mid-Continent asphalt mineral additives months of exposure Months Ratio Months National Bureau outdoor exposures performances Portland Cement Ratio Months Ratio saturated felt shingle smooth-surface specimens specimens after 15 specimens exposed outdoors Stabilized Asphalt Coatings straight asphalt surface specimens tabs thickness Composition Coating thickness mils mils three asphalts type of specimen U.S. Government Printing Venezuela asphalt Viscosity weatherometer tests