Hail Resistance of Roofing ProductsBuilding Research Division, U.S. Institute for Applied Technology, 1969 - 9 pages A test was developed for evaluating the hail resistance of roofings, in which synthetic hailstones (ice spheres) of various sizes were shot at roof assemblies at their free-fall terminal v * elocities.Indentations, granule loss and roofing fracture were observed.The principal conclusion is that:All roofing materials have some resistance to hail damage, but as the size of the hail increases, a level of impact energy is reached at which damage occurs.This level lies in the range of 1 1/2 to 2 inch (3.8-5.1 cm) hailstones for most prepared roofings.(Author). |
From inside the book
Results 1-4 of 4
Page 6
... cracking shingle felt Deck 15 # Felt underlayment Edges Unsupported portion Triple coverage Edges Unsupported portion Triple coverage in cm in ст in cm in ст in cm -in Plywood ..... ( 1 cm ) 14 ( 4.5 ) 134 14 ( 4.5 ) 11/2 ( 3.8 ) in ...
... cracking shingle felt Deck 15 # Felt underlayment Edges Unsupported portion Triple coverage Edges Unsupported portion Triple coverage in cm in ст in cm in ст in cm -in Plywood ..... ( 1 cm ) 14 ( 4.5 ) 134 14 ( 4.5 ) 11/2 ( 3.8 ) in ...
Page 7
... cracking with hailstones 212 - in ( 6.4 cm ) in diameter and smaller , but when insulation was present ( 4c . 4d , 4e , and 4f ) , cracks were pro- duced with 21 / 2 - in ( 6.4 cm ) hailstones . The glass felt roofs fell in between the ...
... cracking with hailstones 212 - in ( 6.4 cm ) in diameter and smaller , but when insulation was present ( 4c . 4d , 4e , and 4f ) , cracks were pro- duced with 21 / 2 - in ( 6.4 cm ) hailstones . The glass felt roofs fell in between the ...
Page 8
... cracked . D , Foamboard delaminated . F , Felts cracked . shattered . - , Not tested . TABLE 4. Threshold of hail ... cracking for brittle roofings and objectionable indentations for metal roofing . Table 4 is a summary of the results ...
... cracked . D , Foamboard delaminated . F , Felts cracked . shattered . - , Not tested . TABLE 4. Threshold of hail ... cracking for brittle roofings and objectionable indentations for metal roofing . Table 4 is a summary of the results ...
Page 9
... cracked below the dents with hailstones larger than 21⁄2 in ( 6.4 cm ) . Note tested . All roofings tested were ... cracking oc- curred when 22 - in ( 6.4 cm ) hailstones were used . This work was sponsored by the Research Committee ...
... cracked below the dents with hailstones larger than 21⁄2 in ( 6.4 cm ) . Note tested . All roofings tested were ... cracking oc- curred when 22 - in ( 6.4 cm ) hailstones were used . This work was sponsored by the Research Committee ...
Common terms and phrases
15 cents air gun apparatus Applied Technology areas of different Asbestos cement asphalt flood coat Asphalt Roofing asphalt shingles automatic data processing building damage Building Research Building Science Series Built-up roofs Bureau of Standards Cement and Concrete Center Class C shingle Coal tar Concrete Properties cracking cylinder dense decks dents DEPARTMENT OF COMMERCE diameter different vulnerability felt damage Fiberboard on 1-in Foamboard free-fall terminal velocity freezing ft 61 cm Gas cylinder Glass fiber insulation hail damage hail resistance hailstone carrier Hailstone Molds Hailstorms ice spheres indentation Institute for Applied interply asphalt Interrelations Between Cement Joules kg/m² kg/m³ large hailstones launcher lb/sq Meteorol microswitches National Bureau Nonbituminous Roofing organic felt polyethylene Portland Cement prepared roofings reported Resistance of Roofing resistant to hail shingles showed Sidney H sizes of hailstones slag solidly supported areas specimen steel decking substrates tested Type 235 shingles U.S. DEPARTMENT U.S. Government Printing velocity 9 ст