Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 67
Page 132
... weight loss for samples placed on test at different times are small and the general trend is maintained . The greatest losses in weight are found with the 2014 - T6 and declad 2024 - T3 alloy samples . The weight losses determined for ...
... weight loss for samples placed on test at different times are small and the general trend is maintained . The greatest losses in weight are found with the 2014 - T6 and declad 2024 - T3 alloy samples . The weight losses determined for ...
Page 220
... weight per unit area ( usually as g / m2 or mg / ft2 ) and commonly referred to as coating weight . The reason for the adoption of coating weight rather than coating thickness as the usual measure of coatings is the difficulty in ...
... weight per unit area ( usually as g / m2 or mg / ft2 ) and commonly referred to as coating weight . The reason for the adoption of coating weight rather than coating thickness as the usual measure of coatings is the difficulty in ...
Page 227
... weight are widely adopted . These methods involve the determination of change in weight of a coated specimen after dissolution of the coating in a suitable medium . Concentrated hydrochloric acid containing 20 g / l of antimony trioxide ...
... weight are widely adopted . These methods involve the determination of change in weight of a coated specimen after dissolution of the coating in a suitable medium . Concentrated hydrochloric acid containing 20 g / l of antimony trioxide ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate