Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 85
Page 57
... potential curves of rotating disc electrodes in ASW at 90 ° C From the alloys tested at 90 ° C , alloys N06625 - Gr ... potential after 60 min , the pitting potential and the repassivation potential provided from cyclic dynamic current ...
... potential curves of rotating disc electrodes in ASW at 90 ° C From the alloys tested at 90 ° C , alloys N06625 - Gr ... potential after 60 min , the pitting potential and the repassivation potential provided from cyclic dynamic current ...
Page 79
... potential was studied . As is well known , the more positive the pitting potential , the more resistant is the alloy . Figure 3 shows potentiostatic pitting potential of alloy 31 in comparison with alloy 317L and alloy 926. As is ...
... potential was studied . As is well known , the more positive the pitting potential , the more resistant is the alloy . Figure 3 shows potentiostatic pitting potential of alloy 31 in comparison with alloy 317L and alloy 926. As is ...
Page 210
... potential from the open circuit potential to -1000 mV / SCE , then returning towards the noble potential until either the current reached .001 amp / cm2 or until the pitting potential was reached . Electrochemical impedance spectroscopy ...
... potential from the open circuit potential to -1000 mV / SCE , then returning towards the noble potential until either the current reached .001 amp / cm2 or until the pitting potential was reached . Electrochemical impedance spectroscopy ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate