... performance of electrodeposited zinc coatings . The corrosion protection afforded by ion vapour deposited aluminium can be improved by the addition of small amounts of zinc and magnesium . 1. INTRODUCTION Sacrificial metal coatings have ...
... performance of electrodeposited zinc coatings . The corrosion protection afforded by ion vapour deposited aluminium can be improved by the addition of small amounts of zinc and magnesium . 1. INTRODUCTION Sacrificial metal coatings have ...
Page 332
... performance improved dramatically as the coating hardness increased . By contrast , erosion performance was not clearly related to the hardness of the material tested . Thus , different responses of the materials were obtained when ...
... performance improved dramatically as the coating hardness increased . By contrast , erosion performance was not clearly related to the hardness of the material tested . Thus , different responses of the materials were obtained when ...
Page 162
... performance and the critical pigment volume concentration slightly decreased . Results indicate that a dispersion time for lamellar micaceous iron oxide of about 4 hours is the best one , and at that time the highest practical adhesion ...
... performance and the critical pigment volume concentration slightly decreased . Results indicate that a dispersion time for lamellar micaceous iron oxide of about 4 hours is the best one , and at that time the highest practical adhesion ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate