Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 38
Page 99
... passive currents decreased , the passive region increased , and the pitting potential became more noble . After one month , an anodic depolarization was observed for all the curves ( Fig . 3 ) being consistent with the literature / 1-3 ...
... passive currents decreased , the passive region increased , and the pitting potential became more noble . After one month , an anodic depolarization was observed for all the curves ( Fig . 3 ) being consistent with the literature / 1-3 ...
Page 107
... passive layers contained more toxic element concentration in the passive layer than in the matrix ( Figs . 6 and 7 ) . However , the effectiveness of the Sn in the passive layer was better than the other toxic elements under the ...
... passive layers contained more toxic element concentration in the passive layer than in the matrix ( Figs . 6 and 7 ) . However , the effectiveness of the Sn in the passive layer was better than the other toxic elements under the ...
Page 371
... passive film reached the surface of the underlying metal , lateral reduction of the passive film along with the metal took place . The overall process was a reversed nucleation growth process as indicated by the inverted anodic peaks in ...
... passive film reached the surface of the underlying metal , lateral reduction of the passive film along with the metal took place . The overall process was a reversed nucleation growth process as indicated by the inverted anodic peaks in ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate