Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 79
Page 179
... measurements when low intensities are required to attain a significant shift from the steady state . Experimental problems encountered in performing current measurements are mainly due to the range choice , which may result in ...
... measurements when low intensities are required to attain a significant shift from the steady state . Experimental problems encountered in performing current measurements are mainly due to the range choice , which may result in ...
Page 180
... measurements under current control and to select the dynamic option to avoid any problems caused by numerical generation of the current intensity . Furthermore , the use of a current ramp has the great advantage of allowing the ...
... measurements under current control and to select the dynamic option to avoid any problems caused by numerical generation of the current intensity . Furthermore , the use of a current ramp has the great advantage of allowing the ...
Page 183
... measurements over the frequency interval [ 6 × 10-3 , 104 ] Hz were carried out using the Ingold reference electrode type 363 ( Argenthal ) . The resistance , R , was determined using a platinum electrode because the AC measurements ...
... measurements over the frequency interval [ 6 × 10-3 , 104 ] Hz were carried out using the Ingold reference electrode type 363 ( Argenthal ) . The resistance , R , was determined using a platinum electrode because the AC measurements ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate