Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 61
Page 2
and fracture processes in engineering structures working in a marine environment . Emphasis is placed on both ... environments . We have used both computational models and experimental procedures either those directly applicable to ...
and fracture processes in engineering structures working in a marine environment . Emphasis is placed on both ... environments . We have used both computational models and experimental procedures either those directly applicable to ...
Page 3
2. CASE HISTORIES OF FRACTURE IN ENVIRONMENTS . - MARINE In this section an analysis is carried out of the causes of corrosion - assisted failures in engineering structures working in marine or similar en- vironments , in order to ...
2. CASE HISTORIES OF FRACTURE IN ENVIRONMENTS . - MARINE In this section an analysis is carried out of the causes of corrosion - assisted failures in engineering structures working in marine or similar en- vironments , in order to ...
Page 146
Coated Steel Panels in a Marine Environment in appearance over the first few months of exposure . The pure zinc coatings , which were bright and shiny before exposure , darkened and after approximately four months they had become ...
Coated Steel Panels in a Marine Environment in appearance over the first few months of exposure . The pure zinc coatings , which were bright and shiny before exposure , darkened and after approximately four months they had become ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate