Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 54
Page 132
... loss for samples placed on test at different times are small and the general trend is maintained . The greatest losses in weight are found with the 2014 - T6 and declad 2024 - T3 alloy samples . The weight losses determined for the 2014 ...
... loss for samples placed on test at different times are small and the general trend is maintained . The greatest losses in weight are found with the 2014 - T6 and declad 2024 - T3 alloy samples . The weight losses determined for the 2014 ...
Page 153
... loss would have been anticipated . Also , since zinc alloys with high nickel levels are more noble than zinc alone they would be expected to suffer less galvanic corrosion . A possible explanation is that the zinc alloys which were ...
... loss would have been anticipated . Also , since zinc alloys with high nickel levels are more noble than zinc alone they would be expected to suffer less galvanic corrosion . A possible explanation is that the zinc alloys which were ...
Page 222
... loss in weight occurs which may be attributed to a non - structural water loss . Dehydration of hopeite and phosphophyllite commences at 80 and 110 ° C respectively and more pronounced weight loss occurs around 115 ° C where hopeite ...
... loss in weight occurs which may be attributed to a non - structural water loss . Dehydration of hopeite and phosphophyllite commences at 80 and 110 ° C respectively and more pronounced weight loss occurs around 115 ° C where hopeite ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate