Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 88
Page 224
... forming elements such as chromium and tungsten / 117 / . Steels with chromium content above 12 % cannot be phosphated . The surface condition and cleaning methods adopted , affect the quality of the coating formed and its properties ...
... forming elements such as chromium and tungsten / 117 / . Steels with chromium content above 12 % cannot be phosphated . The surface condition and cleaning methods adopted , affect the quality of the coating formed and its properties ...
Page 310
... formed as electrochemically active species . However , at higher alkali sulphur solutions , soluble divalent iron sulphur complexes with S22 are formed . Similar attempt made in presence of carbonate ions / 35 / revealed that ...
... formed as electrochemically active species . However , at higher alkali sulphur solutions , soluble divalent iron sulphur complexes with S22 are formed . Similar attempt made in presence of carbonate ions / 35 / revealed that ...
Page 96
... formed appears surrounded by ferrous and zinc phosphate since it has similar crystalline form . The chromic phosphate formed adheres to the ferric phosphate due to the fact that the ionic radius of the iron and chrome are similar ...
... formed appears surrounded by ferrous and zinc phosphate since it has similar crystalline form . The chromic phosphate formed adheres to the ferric phosphate due to the fact that the ionic radius of the iron and chrome are similar ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate