Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 78
Page 132
... exposed to alternate immersion testing for 21 and 42 days are given in Fig . 2. Although the weight losses recorded are much higher than under marine exposure conditions the general trend is repeated with the unclad 2014 and 2024 alloys ...
... exposed to alternate immersion testing for 21 and 42 days are given in Fig . 2. Although the weight losses recorded are much higher than under marine exposure conditions the general trend is repeated with the unclad 2014 and 2024 alloys ...
Page 140
Marine Exposure Conditions under marine exposure conditions . Research is currently in progress to examine the correlation between alternate immersion testing and marine exposure trials for aluminium - lithium alloys . 5. CONCLUSIONS 1 ...
Marine Exposure Conditions under marine exposure conditions . Research is currently in progress to examine the correlation between alternate immersion testing and marine exposure trials for aluminium - lithium alloys . 5. CONCLUSIONS 1 ...
Page 146
... exposure . The pure zinc coatings , which were bright and shiny before exposure , darkened and after approximately four months they had become covered by a thin and tenacious grey / black surface layer . The presence of a few small ...
... exposure . The pure zinc coatings , which were bright and shiny before exposure , darkened and after approximately four months they had become covered by a thin and tenacious grey / black surface layer . The presence of a few small ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate