Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 79
Page 176
... experimental polarization curve and part of the anodic Tafel straight line in the vicinity of the free corrosion potential . The anodic straight line was obtained considering the experimental points relating to the zone examined and the ...
... experimental polarization curve and part of the anodic Tafel straight line in the vicinity of the free corrosion potential . The anodic straight line was obtained considering the experimental points relating to the zone examined and the ...
Page 179
... experimental data . This statement can be verified experimentally if dynamic measurements are performed using the Solartron electrochemical interface model 1286 and the galvanostatic mode . In our case , we always observed a shift of ...
... experimental data . This statement can be verified experimentally if dynamic measurements are performed using the Solartron electrochemical interface model 1286 and the galvanostatic mode . In our case , we always observed a shift of ...
Page 60
... Experimental results and conclusions emanated from different researchers may be not always compared because : a ) Experimental variables such as particle diameter , PVC , types of pigments , additives and binders must be carefully ...
... Experimental results and conclusions emanated from different researchers may be not always compared because : a ) Experimental variables such as particle diameter , PVC , types of pigments , additives and binders must be carefully ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate