Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 79
Page 31
... effects between calcareous scale and microfouling , when applying cathodic protection to metal structures immersed in seawater , has received limited attention in the literature / 4-6 / . The effect of the applied current on bacterial ...
... effects between calcareous scale and microfouling , when applying cathodic protection to metal structures immersed in seawater , has received limited attention in the literature / 4-6 / . The effect of the applied current on bacterial ...
Page 34
... effect of the biofilm on the corrosion potential would make the initiation of crevice corrosion beneath the biofilm more likely . In a recent paper Dexter and Lin / 4 / considered the influence of the biofilm on cathodic protection in ...
... effect of the biofilm on the corrosion potential would make the initiation of crevice corrosion beneath the biofilm more likely . In a recent paper Dexter and Lin / 4 / considered the influence of the biofilm on cathodic protection in ...
Page 116
... effect of CP on the number of bacteria attached is more significant when the applied overpotential increases . The application of CP for SS immersed for 3 and 6 h resulted in an important decrease in cell numbers with respect to the ...
... effect of CP on the number of bacteria attached is more significant when the applied overpotential increases . The application of CP for SS immersed for 3 and 6 h resulted in an important decrease in cell numbers with respect to the ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate