Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 77
Page 132
... determined for the 2014- T3 alloy coupons were less than half those measured for these two alloys and slightly greater than those determined for declad 7075 - T6 . Data for samples exposed to alternate immersion testing for 21 and 42 ...
... determined for the 2014- T3 alloy coupons were less than half those measured for these two alloys and slightly greater than those determined for declad 7075 - T6 . Data for samples exposed to alternate immersion testing for 21 and 42 ...
Page 354
... Determined by Weight Loss MET2 : Corrosion Rate Determined by Linear Polarization MET3 : Corrosion Rate Determined by Variation in Electrical Resistance MET4 : Corrosion Rate Determined by Fe and Cr Control Pressure : 103.42 kPa ...
... Determined by Weight Loss MET2 : Corrosion Rate Determined by Linear Polarization MET3 : Corrosion Rate Determined by Variation in Electrical Resistance MET4 : Corrosion Rate Determined by Fe and Cr Control Pressure : 103.42 kPa ...
Page 356
... determined by weight loss E2 . Probe for corrosion rate determined by variation in electrical resistance E3 : Probe for corrosion rate determined by linear polarization F : Electric heating pad G : Type J termocouple H : Flow control ...
... determined by weight loss E2 . Probe for corrosion rate determined by variation in electrical resistance E3 : Probe for corrosion rate determined by linear polarization F : Electric heating pad G : Type J termocouple H : Flow control ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate