Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 48
Page 32
... deposits and lead to corrosion . It was demonstrated that under abiotic conditions , acetic acid can dissolve protective calcareous deposits and increase current density requirements in ca. 300 mA.cm2 when the metal was polarized at ...
... deposits and lead to corrosion . It was demonstrated that under abiotic conditions , acetic acid can dissolve protective calcareous deposits and increase current density requirements in ca. 300 mA.cm2 when the metal was polarized at ...
Page 34
... deposits on protected surfaces . These deposits decrease the current requirement to achieve complete protection , favoring the cathodic protection effects and increasing the life of sacrificial anodes . The main consequence of biofilm ...
... deposits on protected surfaces . These deposits decrease the current requirement to achieve complete protection , favoring the cathodic protection effects and increasing the life of sacrificial anodes . The main consequence of biofilm ...
Page 125
... deposit formation . Bacterial colonization and pH changes destabilize the calcareous deposits / 20 / , and organic material slows down the precipitation process / 8 / . The presence of organics influences the nature of the scale ...
... deposit formation . Bacterial colonization and pH changes destabilize the calcareous deposits / 20 / , and organic material slows down the precipitation process / 8 / . The presence of organics influences the nature of the scale ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate