Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 36
Page 76
... crevice corrosion in seawater and the critical pitting temperature according to the ASTM G - 48 test respectively . To verify the corrosion resistance further , a multiple crevice assembly test program in natural 30 ° C filtered ...
... crevice corrosion in seawater and the critical pitting temperature according to the ASTM G - 48 test respectively . To verify the corrosion resistance further , a multiple crevice assembly test program in natural 30 ° C filtered ...
Page 240
... crevice corrosion is to be expected on S32750 and S31254 if the temperature or the chlorine concentration exceeds certain limits : thus , at 45 ° C , 2 mg.1-1 chlorine will cause crevice corrosion on both these alloys / 1,2 / . As shown ...
... crevice corrosion is to be expected on S32750 and S31254 if the temperature or the chlorine concentration exceeds certain limits : thus , at 45 ° C , 2 mg.1-1 chlorine will cause crevice corrosion on both these alloys / 1,2 / . As shown ...
Page 242
... crevices while some sulphur was present outside ) . In this way , the sulphide ions bring chemical cathodic protection to the crevice area of stainless steels . It has been reported by others / 11 / that no crevice corrosion was ...
... crevices while some sulphur was present outside ) . In this way , the sulphide ions bring chemical cathodic protection to the crevice area of stainless steels . It has been reported by others / 11 / that no crevice corrosion was ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate