Corrosion Reviews, Volumes 12-13Scientific Publications Division, Freund Publishing House, 1994 |
From inside the book
Results 1-3 of 69
Page 147
... concentration and 34 μm average particle size ( 49.3 % CPVC approximately ) are more appropriate . It is important to realize that , for the two film thicknesses studied , the lower permeability per unit film thickness is observed for ...
... concentration and 34 μm average particle size ( 49.3 % CPVC approximately ) are more appropriate . It is important to realize that , for the two film thicknesses studied , the lower permeability per unit film thickness is observed for ...
Page 151
... concentration are shown in Table 23. Micaceous iron oxide coatings with low pigmentation levels displayed a reduced film permeability . For pigment volume concentrations higher than the critical value ( Table 24 ) film permeability ...
... concentration are shown in Table 23. Micaceous iron oxide coatings with low pigmentation levels displayed a reduced film permeability . For pigment volume concentrations higher than the critical value ( Table 24 ) film permeability ...
Page 162
... concentration up to an optimum value after which the adhesion performance and the critical pigment volume concentration slightly decreased . Results indicate that a dispersion time for lamellar micaceous iron oxide of about 4 hours is ...
... concentration up to an optimum value after which the adhesion performance and the critical pigment volume concentration slightly decreased . Results indicate that a dispersion time for lamellar micaceous iron oxide of about 4 hours is ...
Contents
G Hernández W H Hartt and H A Videla | 30 |
14 | 33 |
Cathodic Protection Criteria and Effectiveness in MIC | 36 |
Copyright | |
24 other sections not shown
Other editions - View all
Common terms and phrases
acid adhesive alkali solutions Alloy 22 Alloy 59 alloy 602CA aluminium anticorrosive application ASTM bacteria bath biocide biofilm biofouling calcareous deposits carbon steel cathodic protection cells chemical chloride composition concentration concrete corrosion attack corrosion inhibitors corrosion potential corrosion protection corrosion rate corrosion resistance crevice corrosion current density effect electrochemical Engineering equipment erosion evaluation experimental film formation galvanized Green Death hydrogen hydrogen embrittlement immersion impact increase industry ions iron laboratory layer maintenance marine environments marine exposure materials mechanical metal surface method NACE Ni-Cr-Mo nickel offshore oxide paint panels particles passive performance phosphate coatings phosphophyllite pigments pipe pitting pitting corrosion polarization curves polarization resistance potentiostatic PTFE reaction rebars reduced reliability rust samples seawater sheet slurry specimens stainless steels stress corrosion cracking structures substrate sulphur Table techniques Technology temperature thickness values velocity Wallpaper-Plus weld zinc phosphate